掺合料混凝土在不同硫酸盐环境中的性能分析

资料大小：380KB
资料类型：.PDF
资料等级：
发布时间：2021-11-20

资料介绍

采用试验室干湿交替快速试验的方法，通过对掺合料混凝土试块外观变化、质量损失、抗压强度的记录和微观结构的扫描。比较
和分析在不同浓度和种类硫酸盐溶液中，掺合料混凝土腐蚀破坏机理；考察和研究硫酸盐浸泡溶液浓度和种类的不同，对掺合料混凝土抗
腐蚀性能的影响。
关键词：掺合料混凝土；硫酸盐侵蚀；干湿交替；SEM
中图分类号： TU528．041 文献标志码： A 文章编号： 1002—3550(2010)05—0003—04
Property analysis of concrete with admixtures under different sulfate environment
L／U Jun，NIU Di—tao，SONG Hua
(CollegeofCivilEngineeringXi’anUniversityofArchitecture& Technology，Xi’an710055，China)
Abstract： By following the experimental cyclic wetting and drying measure，the concrete blocks with adm ixtures are tested by investigating the
mass loss，the compressve strength reduction together with the changes happened on both of the appearan ce an d microstructure．The sulfate corro—
sion m echanism of concrete with admixtures is analyzed by comparing the influences brought by the difference in sulphate types and concentra—
tion．Their specific influences will be outlined as wel1．
Key w ords： concrete with admixtures；sulfate corrosion；wetting an d drying cycle；SEM scanning
0 引言
硫酸盐侵蚀破坏被认为是引起混凝土材料失效破坏的四
大主要因素之一。同时硫酸盐侵蚀也是影响因素最复杂、危害
性最大的一种环境水侵蚀。土壤、地下水、海水以及工业废水中
的硫酸根离子渗入混凝土内部并与水化产物发生反应，产生膨
胀、开裂、剥落等现象，从而使得混凝土的强度和黏性降低并丧
失，严重危害混凝土结构的安全性和耐久性。我国工厂所排放
的废水，东部滨海盐土、海水和西部盐碱环境中的硫酸盐种类、
浓度相差很大；而混凝土在不同种类、浓度的硫酸盐环境下腐
蚀破坏机理也将不同。
在混凝土干湿交替模拟试验中，由于采用硫酸盐浸泡溶液
浓度和种类的不同，得出的结论差异很大。研究fl-嚷明掺合料的
加入能有效降低胶凝材料中 CP．的含量，消耗多余的水化产物
Ca(OH) ，从而改善混凝土抗硫酸盐侵蚀性能。本试验通过模拟
不同浓度和种类硫酸盐环境 (0．5％Na2SO4溶液、2．5％Na2SO4溶
液、5．0％Na SO 溶液和 2．5％MgSO 溶液 )，考察和研究掺合料
混凝土在不同浓度和种类硫酸盐环境中的抗腐蚀性能。
1 试验
1．1 试验材料
原材料为：广州市珠江水泥有限公司旋窑生产的粤秀牌
P·II 42．5R级水泥，化学成分及物理力学性能见表 1、2；粉煤灰
为粤和牌 Ⅱ级粉煤灰，化学成分及物理性能见表 1、3；矿渣采
用马鞍山产矿渣微粉，化学成分及物理性能见表 1、4；减水剂采
用聚羧酸高效减水剂，掺人量为胶凝材料质量的 1％；水为普通
自来水；石子采用陕西泾阳的锤破石(粒径为 5～10mm)，压碎指
标为 12％；砂为陕西灞河中砂，细度模数为 3．0。