低收缩C70自密实大体积混凝土的配制

资料大小：550KB
资料类型：.PDF
资料等级：
发布时间：2021-11-21

资料介绍

分析了复杂型钢组合结构内浇 C70混凝土的特点和难点，按照大掺量粉煤灰高性能混凝土的技术路线进行了混凝土配
合比设计，并对比检测了膨胀剂、减缩剂和内养护剂在变温养护下的功能效果。试验结果表明，掺加一定量的预吸水的内养护剂
后，C70内浇自密实大体积混凝土的自收缩能够满足工程质量控制要求。
关键词：复杂型钢组合结构；低收缩；内养护剂；变温养护
中图分类号：TU528．53 文献标志码：A 文章编号：1002—3550(2015)10—0102—07
Preparation of the low --shrinkage of C70 self--compacting large--volume concrete
YU Chenghang ，HONG ]ingfu ，W AN G Youchao
(Beijing Zhongchao Concrete Co．，Ltd．，Beijing 100024，China)
Abstract：It anaiyzed the characteristics of C70 inner casting concrete and the diffi culties of complex — shaped steel composite structurel，in accordance with the technical line of high—perform ance large—volume fry ash concrete were concrete mix design，and compar —
ison test of expansive agent and shrinkage — reducing agent and internalcuring agent in the functionality under varying temperature
effects．The results show that after adding a certain amount of pre—absorbent water intem ai cunng m aterial，C70 inner casting large—
volum e of autogenous shrinkage of self——compacting concrete can meet the engineering quaiity control requirem ents．
Key words：complex—shaped steel composite structurel；low shrinkage；intemai curing；variable temperature curing
近年来，随着国民经济与建筑技术的高速发展，我国
设计和建设了很多规模大、技术难度高的建筑工程项目。
在这些项目中，大量应用了复杂型钢混凝土组合结构 (巨
柱 )，而且其形式也因为结构设计需要而异常复杂，如外包
或内浇混凝土的多腔箱形、既外包又内浇混凝土的多腔箱
形以及外观为清水混凝土效果的钢管叠合柱等，如此复杂
的型钢}昆凝土组合结构柱，对混凝土的性能、制备和施工
工艺提出了全新的要求。
工程事实表明，若混凝土性能或施工技术对巨柱结构
的复杂性考虑不足时，时常出现内部混凝土与外部型钢产
生脱空等缺陷，甚至在隔板下方出现混凝土不能充分填充
而出现空洞等严重缺陷，这些质量问题将直接影响组合结
构的受力性能，从而影响到建筑结构的整体安全。因此，在
复杂型钢组合结构施工过程中，在慎重选择适宜的施工技
术的同时，更要控制混凝土的自身性能并使之稳定，而且
这一点显得尤为重要。
1 工程概况
北京市 CBD 核心区 Z15地块项目总建筑面积约
43．7万 in ，建筑高度 528 m，地上 108层，地下 7层，竣工
后将成为北京市标志性建筑之一。本工程主体结构体系为
收稿日期：2015—01—04
· 1O2 ·
“巨型外框筒 +内核心筒”，巨型外框筒为 “巨柱 +斜撑 +
转换桁架 +次框架 ”，核心筒为从下到上依次为钢板混凝
土剪力墙、钢支撑混凝土剪力墙和钢筋?昆凝土剪力墙。
高强混凝土结构主要有二部分：巨型组合柱和核心筒
剪力墙。核心筒为钢筋混凝土核心筒，底部区域的混凝土
墙内含钢板及型钢；巨型角柱为钢管混凝土柱，底部区域
的巨型角柱外包混凝土，与其相连的混凝土墙中设钢板及
型钢 (图 1)。巨柱和翼墙的混凝土强度等级为 C70；而且