硅石牺牲混凝土可减少堆芯残骸与混凝土反应的危害性 ，保证我国核 电站的安全运行 。结合台 山核电站实际情况，通过确定原材料、设计配合比，可配制出符合技术规格及相关标准要求的硅石牺牲混凝 土。经 邑测试试验验证，该混凝土性能满足施工技术要求。 关键词 ：堆芯熔融物和混凝土反应 ； 硅石牺牲混凝土 ；含水率 ；配合比 中图分 类号 ：TU528 文献标 志码 ：A 文章编号 ：1000—4726(2015)01—0036—04 RESEARCH OF SILICA SACRIFICE CoNCRETE M IX PROPORTION W ANG Long ，SHILiang f1．China Nuclear Industry Huaxing Construction Co．Ltd．，529228，Taishan，Guangdong，China；2．Jiangsu Research Institute ofBuilding Science，StateKey Laboratory ofHigh Performance CivilEngineering Materials，210008，Nanjing，China) Abstract： Silica sacrincial concrete could reduce the harmfulness caused by reaction between residual reactor core and concrete and protect safe operation of domestic nuclear power station．Based on the practical conditions of Taishan Nuclear Power Plant， silica sacrificial concrete satisfying technical specification and related standards could be produced through determination of raw materials and design of mixing proportion．Performance test proves that the concrete performance successfully satisfies the technical requirements of construction． Keywords： M CCI reaction；silica sacrifice concrete；moisture content；mix proportion 核 电发展在 注重高效的同时 ，安全性也不容忽 视 。我国 引进的第三代核 电站欧洲先进压 水堆 (以 下简称 EPR)吸取三 英里岛与切尔诺 贝利核安全事 故经验，在设计上做了很大改进 ，其最大的特点就 是增加了堆芯熔 融物捕集器 ，以防止在严重事故中 ， 反应堆堆芯熔融物熔 化 、穿透底板 ，造成核污 染。 硅石牺牲混凝 土和硅铁牺牲混凝 土是堆芯熔融物捕 集器 的重要组成部分 ，在反应堆极 端事故时 ，堆 芯 熔融物 和混凝土反应 (以下简称 MCCI反应 )，吸 收放 射性物质 ，降低温度 ，减小反应堆 内压 力 …。 目前 ，世 界上仅有少数 国家成功配 制出了牺牲混 凝 土 ，价格昂贵 我 国牺牲混凝土的基础理论研究薄弱 ， 混凝 土的关键配合比设计方法与制备技术长期被 国 外垄断 。 台山核 电站项 目采用 EPR技术 ，堆芯熔融物 捕 捉 器牺 牲混凝土的配合比设计与制备是实现我国核 电技术自主化 、国产化的关键。本文以硅石牺牲混凝 收稿 日期 ：2014-10-13 基金项 目 ：国家科技支撑计划 (十二五 )资助 (2011BAE27B02) 作者简介 ：王龙 (1968一)，男 ，四川绵阳人 ，工程师 ，实验室主任 ，e—mail： wangUcgs@163．com． 土研制为 目标 ，考虑牺牲混凝土的功能作用及设计要 求 ，从原材料选择、配合比设计及性能测试角度对硅 石牺牲混凝土的开发进行阐述 。 l 硅石牺牲混凝土功能作用及设计要求 1．1 硅石牺牲混凝土的使用部位 硅石牺牲混凝土的使用部位如图 1所示 。

因本站资料资源较多，启用了多个文件服务器，如果浏览器下载较慢，请调用迅雷下载，特别是超过了5M以上的文件！请一定调用迅雷，有时候速度就会飞起哦，如果您的浏览器自动加载了PDF预览，文件太大又卡死，请按下载说明里的把PDF插件关闭了就可以直接下载，不会再预览了！